Название: | Phase formation of oil-well cements based on chemical industry wastes |
Авторы: | Korohodska A. Shabanova H. Logvinkov S. Deviatova N. |
Ключевые слова: | calcium aluminates calcium ferrites calcium aluminoferrites calcium chromite X-ray microprobe analysis solid solutions oil-well cement high strength sulfate resistance |
Дата публикации: | 2023 |
Библиографическое описание: | Korohodska A. Phase formation of oil-well cements based on chemical industry wastes / A. Korohodska, H. Shabanova, S. Logvinkov and other // Сe/papers. – 2023. – Vol. 6. - No. 6. – Р. 69–73. |
Краткий осмотр (реферат): | The crystalline compounds CaAl2O4 and Ca12Al14O33 are reliably identified by electron microscopic and X-ray studies of the structural and phase features of clinker, and the iron- and chromium-containing phases are presented in the form of solid solutions: Ca2Al0.48Fe1.52O5 and Ca5(CrO4)(CrO4)2. This allows creating of a heat-resistant, strong, weighted oil-well cement for cementing “hot” oil and gas wells. It has been found that obtained materials have enhanced strength – compressive strength after 28 days of setting reaches 55 MPa, quick-setting – initial set – 2 hours 55 minutes, final set – 4 hours 20 minutes, quick-setting – compressive strength after 3 days of setting reaches 48.6 MPa, bending strength reaches 6.7 MPa; and are hydraulic binders with water-cement ratio of 0.17 – 0.38; with high sulfate resistance ratio of 1.31 which is 1.5 times higher than that of Portland cement. |
URI (Унифицированный идентификатор ресурса): | http://repository.hneu.edu.ua/handle/123456789/30923 |
Располагается в коллекциях: | Статті (ГРБКТ) |
Файлы этого ресурса:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
Logvinkov SM_Реферат_Phase formation of oil-well cements based on chemical industry wastes.pdf | 76,31 kB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.